Temperature rating

UL224

105℃

Tensile strength 

ASTM D638

≥10.4MPa

Elongation at break

ASTM D638

≥100%

Aging in circulating-air oven 136℃/168h

Tensile strength

ASTM D638

≥7.3MPa

Elongation at break

ASTM D638

≥100%

Volume resistance

ASTM D2671

≥1.0×10¹⁰Ω.cm

Voltage level

UL224

300V / 600V

Dielectric strength

UL224

AC 2500V, 60s, no breakdown

Heat shock

180℃±1℃/4h

No dripping, no flowing, no cracking

Cold bending

-30℃/1h

No cracking, no breaking

Copper corrosion

UL224

No corrosion

300V

600V

5/8

15.9±0.50

0.70±0.15

0.70±0.15

50

9/16

14.3±0.50

0.70±0.15

0.70±0.15

100

1/2

12.7±0.50

0.57±0.15

0.57±0.15

100

7/16

11.1±0.50

0.57±0.15

0.57±0.15

200

3/8

9.53±0.50

0.57±0.15

0.57±0.15

200

5/16

7.92±0.50

0.57±0.15

0.57±0.15

305

0#

8.38±0.50

0.45±0.15

0.57±0.15

305

1#

7.47±0.50

0.45±0.15

0.57±0.15

305

2#

6.68±0.50

0.45±0.15

0.57±0.15

305

3#

5.94±0.30

0.45±0.15

0.57±0.15

305

4#

5.28±0.30

0.45±0.15

0.57±0.15

305

5#

4.72±0.30

0.45±0.15

0.57±0.15

305

6#

4.22±0.30

0.45±0.15

0.57±0.15

305

7#

3.76±0.20

0.45±0.15

0.57±0.15

305

8#

3.38±0.20

0.45±0.15

0.57±0.15

305

9#

3.00±0.20

0.45±0.15

0.57±0.15

305

10#

2.69±0.20

0.35±0.15

0.57±0.15

305

11#

2.41±0.20

0.35±0.10

0.57±0.10

305

12#

2.16±0.20

0.35±0.10

0.57±0.10

305

13#

1.93±0.15

0.35±0.10

0.57±0.10

500

14#

1.68±0.15

0.35±0.10

0.57±0.10

500

15#

1.50±0.15

0.35±0.10

0.57±0.10

500

16#

1.34±0.15

0.35±0.10

0.57±0.10

500

17#

1.19±0.15

0.35±0.10

0.57±0.10

500

18#

1.07±0.15

0.35±0.10

0.45±0.10

500

19#

0.96±0.15

0.35±0.10

0.45±0.10

500

20#

0.86±0.15

0.35±0.10

0.45±0.10

500

21#

0.79±0.15

0.35±0.10

0.45±0.10

500